| Technical Data |
| Product Information |
0.08 mm Thickness Acrylic Adhesive Double side Silicone treated/Polycoated Liner |
| Adhesive Type |
Cross-linked, Tackified Acrylic Adhesives |
| Adhesive Carrier |
Tissue |
| Thickness |
| Tape only |
0.08 mm ± 0.01 mm |
| Release Liner |
0.13 mm ± 0.02 mm |
| Color |
Off-white |
| Release Liner |
Polycoated Paper(printed) |
Peel Adhesion : to stainless steel Room Temperature 180 Angel peel 12 in./min. Jaw speed (305 mm/min)
72 hour Dwell ASTM D-3330 |
1000 grams/25.4mm |
| Static Shear 1 inch2(6.45 cm2) Overlap will hold |
72 °F (22°C) |
| 1,000 grams |
| listed weight for 10,000 min(ASTM D-3654) 10,000 min(ASTM D-3654) |
158 °F (70°C) |
| Liner Release 1 inch(25.4 mm) width Jaw Speed : 12 inch/min (305 mm/min) |
Max. 50 grams |
| Temperature Resistance |
| Short Term(minutes, hours) |
120°C |
| Long Term(Days, Weeks) |
80°C |
| Solvent Resistance |
Adhesion to Stainless steel, % adhesion retention,100 hour immersion 12 inch/min(305 mm/min) rate of peel, |
| Available Sizes Standard roll Length |
50 M/100/200M |
| Roll width |
1,200 mm |
| Slitting Tolerance |
±0.8 mm |
| Application Techniques |
- Bond strength is dependent upon the amount of adhesive-tosurface contact developed. Firm application pressure help develop better adhesive contact and improve bond strength.
- To obtain optimum adhesion, the bonding surfaces must be cleaned, dry and well unified. Typical surface cleaning solvents are isopropyl alcohol and water(rubbing alcohol) or heptane. Note : Be sure to follow the manufacturer’s precautions and direction for use when using solvents
- Ideal tape application temperature range is 70°C (22°C) to 100°F (38°C). Initial tape
|